Green death

For the Doctor Who serial, see The Green Death.

Green death is a solution used to test the resistance of metals and alloys to corrosion. It consists of a mixture of sulfuric acid, hydrochloric acid, iron(III) chloride and copper(II) chloride and its boiling point is at approximately 103 °C. Its typical chemical composition is given in the table hereafter:[1][2][3][4]

Chemical composition of the green death solution

Reagent (—)	Formula (—)	Usually (wt. %)	Min (wt. %)	Max (wt. %)
Sulfuric acid	H2SO4	11.9	11.5	11.9
Hydrochloric acid	HCl	1.3	1.2	1.3
Iron(III) chloride	FeCl3	1.0	1.0	1.0
Copper(II) chloride	CuCl2	1.0	1.0	1.0

The chemical composition of the green death solution allows it to achieve a particularly aggressive oxidizing chloride solution.[1] Indeed, among the four reagents, all are oxidizing species (H₂SO₄, Fe^3+, Cu^2+) except hydrochloric acid (HCl) in which the chlorine atom is present in its lowest oxidation state as Cl^− anion. The chloride anions, also added to the solution as counter-ions of iron(III) and copper(II) species, are very aggressive for the localized corrosion of metals and alloys as they induce severe pitting corrosion problems. The green death solution is also used to determine the critical pitting temperature (CPT) and the critical crevice temperature (CCT) of metals and alloys.^[citation needed]

See also

• Aqua regia – Mixture of nitric acid and hydrochloric acid in a 1:3 molar ratio
• Piranha solution – Oxidizing acid mixture containing sulfuric acid and hydrogen peroxide

References

1. Corrosionpedia (14 November 2016). "What is Green Death? – Definition from Corrosionpedia". Corrosionpedia. Retrieved 10 September 2021.
2. Haynes International. "Resistance to pitting and crevice corrosion of Hastelloy C-276". Haynesintl.com. Retrieved 10 September 2021.
3. Specialmetals.com. "Inconel alloy C-276" (PDF). Specialmetals.com. Retrieved 10 September 2021.
4. Mottu, Nathalie (2016). URTM66, 02/2016, Industeel ArcelorMittal.